Our MD-C101 range of Maleic Anhydride grafted PP products are carefully formulated using a specialized process that produces   a very stable product with high functionality, extremely low volatility and odor.

Our MD-C101 range of Maleic Anhydride grafted PP products are carefully formulated using a specialized process that produces   a very stable product with high functionality, extremely low volatility and odor.

Features

 Grade

Date

FH116

FH118

FH1012

FH1016

Test Method

Unit

MFI

100-130

90-130

90-120

450-550

ASTM D1238

g/10min

Grafting Level

0.5-1.0

0.7-1.0

0.5-0.8

1.0-1.2

NZG-M-1309

wt%

Base Resin

PP-H

PP-B

PP-R

 

 

 

 Grade

Date

FH116

FH118

FH1012

FH1016

Test Method

Unit

MFI

100-130

90-130

90-120

450-550

ASTM D1238

g/10min

Grafting Level

0.5-1.0

0.7-1.0

0.5-0.8

1.0-1.2

NZG-M-1309

wt%

Base Resin

PP-H

PP-B

PP-R

 

 

 
Specifications

PP+GF30 3%coupling agent

 

Tensile

Flexural

Flexural

Izod impact

 

strength

strength

modulus

strength

 

MPa

MPa

MPa

MPa

FH116

92

128

5200

15

FH118

90

126

5150

17

PP+GF30 3%coupling agent

 

Tensile

Flexural

Flexural

Izod impact

 

strength

strength

modulus

strength

 

MPa

MPa

MPa

MPa

FH116

92

128

5200

15

FH118

90

126

5150

17
Instructions

4.1 Coupling agent：Suitable for long glass fiber (LFT), talc, calcium carbonate, mica, aluminum/magnesium hydroxide filled PP compounds.                        

A loading of 2.0-8.0% can significantly improve the mechanical and heat resistant properties.

4.2 Polarity Enhancer：Increases the polarity of PP. A loading of 10-20% will significantly improve the dyeing property and viscosity of PP.

 

4.1 Coupling agent：Suitable for long glass fiber (LFT), talc, calcium carbonate, mica, aluminum/magnesium hydroxide filled PP compounds.                        

A loading of 2.0-8.0% can significantly improve the mechanical and heat resistant properties.

4.2 Polarity Enhancer：Increases the polarity of PP. A loading of 10-20% will significantly improve the dyeing property and viscosity of PP.

 