PA66 Flame Retardant UL94 V0

Test method

MD-F147

MD-148

MD-149

MD-150

MD-151

Density (g/cm3)

ISO1183

1.39

1.41

1.63

1.41

1.18

Filler content(%)

ISO1172

GF25

GF25

GF30

GF30

---

Mold shrinkage (%)

ISO294  Parallel

0.3

0.3

0.2

0.2

1.2

ISO294  Vertical

0.7

0.7

0.6

0.6

1.8

Tensile breaking strength (MPa)

ISO527  50mm/min

135

140

170

155

75

Elongation at break (%)

ISO527  50mm/min

2

2

2.2

2.3

2

Flexual strength (MPa)

ISO178        23℃ 10mm/min

200

200

250

220

100

Flexual modulus (MPa)

ISO178        23℃ 10mm/min

8200

7800

9300

8500

3200

Notched Izod impact strength (JK/㎡）

ISO180  23℃

8

6

10

7.5

3

Izod impact strength

ISO179  23℃

50

40

60

50

50

Melting point (℃)

ISO11357-1

260

260

260

260

260

Distortion temperature (℃)

ISO75   0.45Mpa

250

250

250

250

250

ISO75   1.8Mpa

245

245

245

245

75

UL Flammability

UL-94

V0

V0

V0

V0

V0

Glow-wire ignition temperature

IEC 60695-2-13

775

775

875

775

775

Surface resistivity (Ω)

IEC60093

1.00E+14

1.00E+14

1.00E+14

1.00E+14

1.00E+14

Volume resistivity(Ω.cm)

IEC60093

1.00E+15

1.00E+15

1.00E+15

1.00E+15

1.00E+15