Functional Masterbatch for nylon 66 cable tie

MD-N066

Features

Production Introduction:

MD-N66 is specially designed for cable tie with low-temperature and delivers lower raw material cost, excellent flowability, faster cycle, low-temperature resistance and easier mold release compared to toughened Nylon 66 resin resulting in higher productivity and enhanced design freedom for injection molding customers. This grade also permits production of molded parts with good initial color plus color retention when using regrind.

MD-N66 can be used for other thin-wall injection molding applications, including: Connectors, Plug housings, PCB spacers, Window components, and so on.

Production Introduction:

MD-N66 is specially designed for cable tie with low-temperature and delivers lower raw material cost, excellent flowability, faster cycle, low-temperature resistance and easier mold release compared to toughened Nylon 66 resin resulting in higher productivity and enhanced design freedom for injection molding customers. This grade also permits production of molded parts with good initial color plus color retention when using regrind.

MD-N66 can be used for other thin-wall injection molding applications, including: Connectors, Plug housings, PCB spacers, Window components, and so on.

Specifications

Items	Test Method	Unit	Results （DAM）
Physical Properties
Specific gravity	ASTM D-792		1.12
Mold shrinkage	ASTM D-955	%	1.0
Moisture uptake (24 hrs)	ASTM D-570	%	1.2
Mechanical Properties
Tensile modulus, 23℃	ASTM D-638	MPa(psi)	1900 (275,000)
Tensile strength @ yield, 23°C	ASTM D-638	MPa(psi)	65 (9500)
Elongation @ break, 23°C	ASTM D-638	%	>20
Flexural modulus, 23°C	ASTM D-790	MPa(psi)	2000 (29,000)
Flexural strength, 23°C	ASTM D-790	MPa(psi)	85 (12,500)
Notched izod impact strength, 23°C	ASTM D-256	J/M	100

Below data are based on 20% MD-N066 blended with 80% Nylon 66

Items	Test Method	Unit	Results （DAM）
Physical Properties
Specific gravity	ASTM D-792		1.12
Mold shrinkage	ASTM D-955	%	1.0
Moisture uptake (24 hrs)	ASTM D-570	%	1.2
Mechanical Properties
Tensile modulus, 23℃	ASTM D-638	MPa(psi)	1900 (275,000)
Tensile strength @ yield, 23°C	ASTM D-638	MPa(psi)	65 (9500)
Elongation @ break, 23°C	ASTM D-638	%	>20
Flexural modulus, 23°C	ASTM D-790	MPa(psi)	2000 (29,000)
Flexural strength, 23°C	ASTM D-790	MPa(psi)	85 (12,500)
Notched izod impact strength, 23°C	ASTM D-256	J/M	100

Below data are based on 20% MD-N066 blended with 80% Nylon 66

Instructions

Typical Properties(20% MB plus 80% PA66)

Values shown are based on limited testing. These provisional values are not intended for use in establishing maximum, minimum or ranges for specification purposes. Properties were measured at 23°C unless otherwise specified.

Typical Properties(20% MB plus 80% PA66)

Values shown are based on limited testing. These provisional values are not intended for use in establishing maximum, minimum or ranges for specification purposes. Properties were measured at 23°C unless otherwise specified.