PC Transparent Flame Retardant Masterbatch MD-F102

MD-F102 is the dedicated high transparent resin, halogen-free / low-halogen flame retardant, the masterbatch is transparent granule. This applies to transparent or opaque PC flame retardant V0, PC fiber flame retardant V0, light diffusion PC flame retardant V0 (LED lampshade, lamp tube, lamp hold, bulb.) It does not affect the light transmittance and haze.

CONTACT US

Features

Advantage:

Small amount of addition.

The physical properties of small influence on PC; hardly affect transparent clear PC performance; Good thermal stability; TGA decomposition temperature is high.

Mixing with the PC materials, direct injection molding to obtain flame retardant PC products.

Use MD-F102 could reduce your cost by 20%-30%. Save your costs. Interaction mechanism:

MD-F102 Is a halogen-free , low-halogen polymer grade flame retardant masterbatch, when PC combustion can promote the release of CO2 and H2O, promoting polyphenols, aliphatic and aromatic substances generated to accelerate the rate of carbon into the PC, and prevent combustible gases propagation and heat release, to achieve the flame retardant effect.

Advantage:

Small amount of addition.

The physical properties of small influence on PC; hardly affect transparent clear PC performance; Good thermal stability; TGA decomposition temperature is high.

Mixing with the PC materials, direct injection molding to obtain flame retardant PC products.

Use MD-F102 could reduce your cost by 20%-30%. Save your costs. Interaction mechanism:

MD-F102 Is a halogen-free , low-halogen polymer grade flame retardant masterbatch, when PC combustion can promote the release of CO2 and H2O, promoting polyphenols, aliphatic and aromatic substances generated to accelerate the rate of carbon into the PC, and prevent combustible gases propagation and heat release, to achieve the flame retardant effect.

Specifications

PC Transparent Flame Retardant Masterbatch MD-F102 Properties V0 flame retardant transparent PC resin typical data

Direct injection molding applications recipe table
Material	Specification			Addition Ratio
PC	110(%)			100
FR-501M	(%)			6
Application data
Properties	Test items	Units	Test Condition	1#
Flammability	Vertical flame test	1.6mm	UL94	V0
Transparency	-	-	-	transparent
Mechanical Properties	Notched impact strength	KJ/m2	GB/T1843	65
	Notched impact strength	J/m	ASTM D256	830
	Bending strength	Mpa	GB/T1041	98
	Tensile Strength	Mpa	GB/T1040	60
	Breaking elongation	%	GB/T1040	95

PC Transparent Flame Retardant Masterbatch MD-F102 Properties V0 flame retardant transparent PC resin typical data

Direct injection molding applications recipe table
Material	Specification			Addition Ratio
PC	110(%)			100
FR-501M	(%)			6
Application data
Properties	Test items	Units	Test Condition	1#
Flammability	Vertical flame test	1.6mm	UL94	V0
Transparency	-	-	-	transparent
Mechanical Properties	Notched impact strength	KJ/m2	GB/T1843	65
	Notched impact strength	J/m	ASTM D256	830
	Bending strength	Mpa	GB/T1041	98
	Tensile Strength	Mpa	GB/T1040	60
	Breaking elongation	%	GB/T1040	95

Instructions

Directly Mixing the materials, inject mold. Or single-screw extruder modified material. Reference ratio amount:3%-8%. Or according to products.

Package and storage:

Paper bags lined with plastic bag, Net weight for each bag:25kgs.

Keep in a dry and ventilated place to prevent sun exposure, water, moisture. Shelf life of 12 months, please sealed after not using up.

Directly Mixing the materials, inject mold. Or single-screw extruder modified material. Reference ratio amount:3%-8%. Or according to products.

Package and storage:

Paper bags lined with plastic bag, Net weight for each bag:25kgs.

Keep in a dry and ventilated place to prevent sun exposure, water, moisture. Shelf life of 12 months, please sealed after not using up.